C14500, or tellurium copper, has similar Mechanical properties to unalloyed, pure copper but with a higher machinability. The cutting properties of C14500 are enhanced significantly by creating a copper alloy with the addition of tellurium. Tellurium copper is also known for its high electrical conductivity characteristic.

C14500 spec sheet C14500 size schedule Weight calculator Standard products

C14500

Product description: Tellurium copper
Tempers: H02 half hard, H04 hard
Solids: 3/8" to 2 3/4" O.D.*
Standard lengths: 144"   *Consult mill for other sizes

Typical uses

Architecture: fire protection
Electrical: electrical connectors, motor parts, soldering copper, switch parts, transistor bases
Industrial: forgings, furnace brazed articles, screw machine products, soldering tips, welding torch tips
Plumbing: fixtures, plumbing fittings, sprinkler heads

Similar or equivalent specification

CDA ASTM SAE AMS Federal Military Other
C14500 B124
B124M
B301
B301M		 J461
J463		       Tellurium-bearing (PTE)

Chemical composition

Cu%1,2 P% Te%
Chemical composition according to ASTM B301/B301M-13(2020)

1Includes silver   2Includes tellurium and phosphorus
Note: includes oxygen-free or deoxidized grades with deoxidizers (such as phosphorus, boron, lithium, or other) in an amount agreed upon. Unless otherwise noted, single values represent maximums.
99.90
min		 0.004-
0.012		 0.40-
0.70

Machinability

Copper alloy UNS no. Machinability rating Density (lb/in3 at 68 °F)
C14500 85 0.323

Mechanical properties

Mechanical properties according to ASTM B301/B301M-13(2020)

C14500

H02 half hard

Size range: 1/16" diameter rod to 1/4" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load, min Elongation, 4x diameter or specimen thickness, min Brinell hardness (500 kg load) Remarks
Ksi MPa Ksi MPa % typical BHN  
38 260 30 205 8 76  
Size range: over 1/4" diameter rod to 2 5/8" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load, min Elongation, 4x diameter or specimen thickness, min Brinell hardness (500 kg load) Remarks
Ksi MPa Ksi MPa % typical BHN  
38 260 30 205 12 76  

C14500

H04 hard

Size range: 1/16" diameter rod (round only) to 1/4" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load, min Elongation, 4x diameter or specimen thickness, min Brinell hardness (500 kg load) Remarks
Ksi MPa Ksi MPa % typical BHN  
48 330 40 275 4 81  
Size range: over 1/4" diameter rod (round only) to 1 1/4" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load, min Elongation, 4x diameter or specimen thickness, min Brinell hardness (500 kg load) Remarks
Ksi MPa Ksi MPa % typical BHN  
44 305 38 260 8 81  
Size range: over 1 1/4" diameter rod (round only) to 3" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load, min Elongation, 4x diameter or specimen thickness, min Brinell hardness (500 kg load) Remarks
Ksi MPa Ksi MPa % typical BHN  
40 275 35 240 8 81  

Physical properties

Physical properties provided by CDA
  US Customary Metric
Melting point - liquidus 1976 °F 1080 °C
Melting point - solidus 1924 °F 1051 °C
Density 0.323 lb/in3 at 68 °F 8.94 gm/cm3 at 20 °C
Specific gravity 8.94 8.94
Electrical conductivity 93% IACS at 68 °F 0.539 MegaSiemens/cm at 20 °C
Thermal conductivity 205 Btu/sq ft/ft hr/°F at 68 °F 355 W/m at 20 °C
Coefficient of thermal expansion 68-212 9.5 · 10-6 per °F (68-212 °F) 16.5 · 10-6 per °C (20-100 °C)
Coefficient of thermal expansion 68-392 9.7 · 10-6 per °F (68-392 °F) 16.8 · 10-6 per °C (20-200 °C)
Coefficient of thermal expansion 68-572 9.9 · 10-6 per °F (68-572 °F) 17.1 · 10-6 per °C (20-300 °C)
Specific heat capacity 0.092 Btu/lb/°F at 68 °F 385.5 J/kg at 20 °C
Modulus of elasticity in tension 17000 ksi 117212 MPa
Modulus of rigidity 6400 ksi 44127 MPa

Fabrication properties

Fabrication properties provided by CDA
Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene welding Fair
Gas shielded arc welding Fair
Coated metal arc welding Not recommended
Spot weld Not recommended
Seam weld Not recommended
Butt weld Fair
Capacity for being cold worked Good
Capacity for being hot formed Good
Forgeability rating 65
Machinability rating 85

Thermal properties

Thermal properties provided by CDA
*Temperature is measured in Fahrenheit.
Treatment Minimum* Maximum*
Annealing 800 1200
Hot treatment 1400 1600

Common fabrication processes

Cold - drawing, machining, moderate cold heading; Hot - extrusion, forging (closed die only)

Common fabrication processes provided by CDA

Find a product

Search by
CDA number

Request a quote
C14500 C23000 C24000 C26000 C31400 C31600 C46400 C51000 C52100 C53400 C54400 C62400 C63000 C63020 C64200 C64210 C65100 C67300 C67400 C67410 C67600 C69300 C69400 C69430 C72900 (AMS 4596) C72900 (AMS 4597)
C72900 (AMS 4598) C83600 C83800 C84200 C84400 C84800 C85700 C86200 C86300 C86400 C86500 C86700 C87850 C89320 C89325 C89520 C89831 C89833 C89835 C89844 C90300 C90500 C90700
C90800 C91000 C91100 C91300 C91600 C91700 C92200 C92300 C92500 C92700 C92800 C92900 C93200 C93400 C93500 C93600 C93700 C93800 C93900 C94000 C94100 C94300 C94700
C94700HT C94800 C95200 C95300 C95300HT C95400 C95400HT C95410 C95410HT C95500 C95500HT C95510 C95520HT C95600 C95800 C95900 C96400 C96900HT C97300 C97600 C97800 C99500 CONCAST380
✖